Improvement of the reactivity of triethyl phosphate and structural behavior of hydroxyapatite versus the synthesis conditions by sol–gel route

Malika Merzougui, Fatima Zohra Mezahi, Achour Dakhouche, Djelel Kherifi, and Foudil Sahnoune

Physics and Chemistry of Materials Laboratory, Department of Physics, Mohamed Boudiaf University, M’sila, Algeria

 

E-mail: fatimazohra.mezahi@univ-msila.dz

Received: 19 June 2021  Accepted: 12 October 2021

Abstract:

Hydroxyapatite (HA) is a biocompatible and bioactive material used as bone-substitute materials in both orthopedics and dentistry. This work is devoted to studying the synthesis of hydroxyapatite (HA) by sol–gel route using triethyl phosphate (TEP) and calcium nitrate tetrahydrate as calcium and phosphor precursors. In order to optimize the hydrolysis of TEP, each prepared solution was aged in a closed Teflon® container. Several factors were tested in order to improve the synthesis conditions of well-crystallized HA. The effect of aging time (4 h, 16 h, and 24 h), aging temperature (25 °C, 50 °C, 70 °C, and 90 °C) of the prepared solutions, and the type of solvents (ethanol and/or distilled water) were tested. All dried gels were calcined at 700 °C for 1 h. The obtained results showed that the crystallinity degree of hydroxyapatite increases with aging time and temperature, which must not exceed 70 °C. When the prepared solutions were aged at 90 °C, the tri-calcium phosphate (TCP) was formed as a major phase and HA was present as a very minor phase. It was remarked that the aging of sols in a closed Teflon container® leads to an important decrease of the aging time and temperature. It was found that 24 h and 70 °C are the optimal conditions for the synthesis of well-crystallized HA. Also, it was deduced that a sufficient amount of water was needed to hydrolyze the triethyl phosphate and consequently, to obtain a well-crystallized HA.

Keywords: Sol–gel; Hydroxyapatite; Hydrolysis; Aging time; Aging temperature; Solvent

Full paper is available at www.springerlink.com.

DOI: 10.1007/s11696-021-01938-8

 

Chemical Papers 76 (2) 1045–1061 (2022)

Saturday, May 18, 2024

IMPACT FACTOR 2021
2.146
SCImago Journal Rank 2021
0.365
SEARCH
Advanced
VOLUMES
European Symposium on Analytical Spectrometry ESAS 2022
© 2024 Chemical Papers